PENGARUH PENGGUNAAN LIMBAH AMPAS TEBU (BAGASSE ASH) SEBAGAI BAHAN POZZOLAN PADA BETON RINGAN

M. Hifzni Alfain; Ely Mulyati

doi:10.31869/rtj.v9i2.7907

PENGARUH PENGGUNAAN LIMBAH AMPAS TEBU (BAGASSE ASH) SEBAGAI BAHAN POZZOLAN PADA BETON RINGAN

M. Hifzni Alfain, Ely Mulyati

Sari

This study aims to analyze the effect of using sugarcane bagasse ash (BA) as a partial substitute for cement in lightweight concrete mixtures. The experimental method was conducted with variations of BA substitution at 0% (normal), 2.5%, 3.5%, and 4.5% of the cement weight. The tests included slump test, compressive strength at 7, 21, and 28 days, and split tensile strength at 28 days. The results showed that the use of BA up to 4.5% still met the workability requirements according to SNI 1972:2008 with slump values ranging from 7.2-8.2 cm. The optimal compressive strength was achieved at 3.5% BA substitution with values of 8.77 MPa (7 days), 26.31 MPa (21 days), and 28.58 MPa (28 days), representing an increase of 14.8%, 9.0%, and 7.1% respectively compared to normal concrete. Similarly, the split tensile strength reached its highest value of 2.36 MPa at 3.5% BA substitution. The study concludes that 3.5% BA substitution is the optimal proportion for producing lightweight concrete with improved mechanical properties while maintaining good workability.

Keywords: compressive strength, lightweight concrete, pozzolan, split tensile strength, sugarcane bagasse ash

Teks Lengkap:

PDF

Referensi

Arumningsih, D., Joko Priyanto, K., & Gunarso. (2023). Inovasi Beton Ringan Dan Ekonomis Menggunakan Abu Sekam Padi, Serbuk Bata Ringan, Abu Batu. Jurnal Teknik Sipil Dan Arsitektur, 28(2), 54–60. https://doi.org/10.36728/jtsa.v28i2.2587

Bahurudeen, A., & Santhanam, M. (2015). Influence of different processing methods on the pozzolanic performance of sugarcane bagasse ash. Cement and Concrete Composites, 56, 32–45. https://doi.org/https://doi.org/10.1016/j.cemconcomp.2014.11.002

BSN. (2008). SNI 1972:2008 Cara Uji Slump Beton. Jakarta: Badan Standardisasi Nasional.

Budhi Rahardja, I., Nia Surbakti, V. C., & Siregar, A. L. (2022). Empowering Abu Cangkang Kelapa Sawit Terhadap Kualitas Bata Beton Ringan (Light-Weight Concrete). Jurnal Teknologi, 14(1), 119–126. https://jurnal.umj.ac.id/index.php/jurtek/article/view/11050

Mulyati, E., & Anggriani, M. (2022). Pengaruh Pemanfaatan Abu Ampas Tebu dan Kawat Bendrat Terhadap Kuat Tekan dan Kuat Lentur Beton Ringan. Jurnal Teknik Sipil, 29(2), 199–206. https://doi.org/10.5614/jts.2022.29.2.11

Nasarudin, N., Rahayu, M., Asyari, D. P., Sofyan, A., Fadli, M., Hari, K. K., Nehe, B. M., Udaya, L. O. M. R. A., Yelfiza, Y., Mulyati, E., & others. (2024). Metode Penelitian Kombinasi (Mixed Method). CV. Gita Lentera.

Purnawirati, I. G. . N., & Moi, F. (2021). Penggunaan Variasi Abu Terbang dan Superplasticizer Dalam Pembuatan Beton Ringan Struktur. Jurnal Talenta Sipil, 4(1), 74. https://doi.org/10.33087/talentasipil.v4i1.51

Sandra Melly, Iranita Haryono, Ely Mulyati, et. all. (2020). Manajemen Proyek Buku SBN. In Journal GEEJ (Vol. 7, Issue 2).

Saputra, K., & Mulyati, E. (2024). Pengaruh Subsitusi Ampas Tebu Pada Fly Ash Terhadap Kuat Tekan Mortar Geopolimer. 10(2), 115–123.

Zakariya, M. E., & Risdianto, Y. (2018). Pengaruh Penambahan Serat Sabut Kelapa Dengan Penggunaan Catalyst, Monomer, Dan Fly Ash Sebagai Material Penyusun Beton Ringan Seluler. Jurnal Rekayasa Teknik Sipil, 1(1), 209–215.

DOI: https://doi.org/10.31869/rtj.v9i2.7907